钛酸钾晶须耐碱多孔陶瓷的制备及表征(英文)
100 积分
50
评分
4.8 积分- 详情
- 2021-04-28
- 简介
pdf
- 428KB
- 页数 6P
- 阅读 93
- 下载 36
The preparation and characterization of alkaline resistant porous ceramics from potassium titanate whiskers are studied.K2Ti4O9 whiskers in the whisker preforms(mixtures of K2Ti6O13 and K2Ti4O9)were com- pletely converted to K2Ti6O13 at 960℃.The alkaline resistance as well as the change in bending strength,porosity and permeability of the ceramics was investigated by altering the composition of the preforms in which the content of K2Ti6O13 whiskers was higher than 50%(molar fraction).The alkaline resistance of the porous K2Ti6O13 ceram-ics is found much higher than that of Al2O3 in caustic NaOH solutions,and further study indicates that the K2Ti6O13 ceramics can be stably used in solutions of pH>2.0.The bending strength increases initially with the content of the raw K2Ti6O13 in the preforms up to 66%(molar fraction)and then decreases,contrary to the behaviors of porosity and permeability.The values of bending strength,porosity and permeability of the ceramics prepared from the pre-form of 80%(molar fraction)raw K2Ti6O13 whiskers are respectively 56MPa,29.4%and 330L·m-2 ·h-1 ,which are comparable to those of the porous Al2O3 ceramics.
对不起，您暂无在线预览权限，如需浏览请
立即登录热门商品
相关推荐
钛酸钾晶须耐碱多孔陶瓷的制备及表征(英文) 428KB
硼酸镁晶须多孔陶瓷膜支撑体的制备方法 111KB
多孔陶瓷材料的制备技术 1.9MB
碳化硅多孔陶瓷的制备研究 359KB
粉煤灰基多孔陶瓷对孔雀石绿的脱色研究(英文) 347KB
硅藻土多孔陶瓷膜管的研制和性能表征 75KB
氧化铝质多孔陶瓷制备工艺及应用 1.9MB
多孔吸音陶瓷的制备 495KB
碳化硅_堇青石多孔陶瓷的制备及其性能 1.8MB
86Al2O3多孔陶瓷的制备和性能研究 1.1MB